Search Results

NOx emissions have traditionally been difficult to control from diesel engines; however, lean NOx trap catalysts have been shown to reduce NOx emissions from diesel engines by greater than 90% under some conditions. It is imperative that lean NOx traps be highly selective to N2 to achieve the designed NOx emissions reduction. If selectivity for NOx reduction to NH3 or N2O is significant then, ultimately, higher levels of pollution or greenhouse emissions will result. Here studies of the N2 selectivity of lean NOx trap regeneration with in-cylinder techniques are presented. Engine dynamometer studies with a light-duty engine were performed, and a lean NOx trap in the exhaust system was regenerated by controlling in-cylinder fuel injection timing and amounts to achieve rich exhaust conditions. NH3 and N2O emissions were analyzed with FTIR spectroscopy.

An operational challenge associated with SCR catalysts is the NH3 slip control, particularly for commercial small pore Cu-zeolite formulations as a consequence of their significant ammonia storage capacity. The desorption of NH3 during increasing temperature transients is one example of this challenge. Ammonia slipping from SCR catalyst typically passes through a platinum based ammonia oxidation catalyst (AMOx), leading to the formation of the undesired byproducts NOx and N2O. We have discovered a distinctive characteristic, an overlapping NH3 desorption and oxidation, in a state-of-the-art Cu-zeolite SCR catalyst that can minimize NH3 slip during temperature transients encountered in real-world operation of a vehicle.

A set of elementary surface reactions is proposed for modeling the chemistry in a lean NOx trap during regeneration (reduction of stored NOx). The proposed reaction mechanism can account for the observed product distribution from the trap over a range of temperatures and inlet gas compositions similar to those expected for realistic operation. The mechanism includes many reactions already discussed in the literature, together with some hypothesized reactions that are required to match observations from temperature programmed reactor experiments with a commercial lean NOx trap catalyst. Preliminary results indicate that the NOx trap regeneration and byproduct formation rates can be effectively captured by using a relatively compact set of elementary reactions.

Development of a microwave-regenerated particulate filter system has evolved from bench scale work to actual diesel engine experimentation. The filter system was initially evaluated on a stationary mounted 1.2-L diesel engine and was able to remove a significant amount of carbon particles from the exhaust. The ability of the microwave energy to regenerate or clean the filter was also demonstrated on this engine under idle conditions. Based on the 1.2-L experiments, improvements to the filter design and materials were implemented and the system was re-evaluated on a vehicle equipped with a 7.3-L diesel engine. The 7.3-L engine was selected to achieve heavy filter loading in a relatively short period of time. The purpose of these experiments was to evaluate filter-loading capacity, power requirements for regeneration, and filter regeneration efficiency. A more detailed evaluation of the filter was performed on a stationary mounted 1.9-L diesel engine.

Metal Compression Forming (MCF) is a variant of the squeeze casting process, in which molten metal is allowed to solidify under pressure in order to close porosity and form a sound part. However, the MCF process applies pressure on the entire mold face, thereby directing pressure on all regions of the casting and producing a uniformly sound part. The process is capable of producing parts with properties close to those of forgings, while retaining the near net shape, complexity in geometry, and relatively low cost of the casting process. The paper describes the casting process development involved in the production of an aluminum A357 alloy motor mount bracket, including the use of a filling and solidification model to design the gating and determine process parameters. Tensile properties of the component are presented and correlated with those of forged components.

Urea-SCR systems are potentially a highly-effective means of NOX reduction for light-duty diesel vehicles. However, use of urea-SCR technologies at low temperatures presents unique technical challenges. This study was undertaken to provide more knowledge about low temperature urea decomposition and the resulting effects on SCR performance. Data are presented for experiments using two SCR catalysts of differing size with a light-duty diesel engine. Analyses of the NOX reduction efficiency, NH3 storage phenomena, and unregulated emissions are shown. Over production of NO2 by the oxidation catalyst is demonstrated to be problematic at 25,000 hr-1 space velocity for a range of temperatures. This leads to production of N2O by both SCR catalysts that is higher when urea is injected than when NH3 is injected.

Aluminum alloys containing cerium have excellent castability and retain a substantial fraction of their room temperature strength at temperatures of 200°C and above. High temperature strength is maintained through a thermodynamically trapped, high surface energy intermetallic. Dynamic load partitioning between the aluminum and the intermetallic increases mechanical response. Complex castings have been produced in both permanent mold and sand castings. This versatile alloy system, using an abundant and inexpensive co-product of rare earth mining, is suitable for parts that need to maintain good properties when exposed to temperatures between 200 and 315°C.

Accurate knowledge of diesel particulate filter (DPF) particulate matter (PM) loading is critical for robust and efficient operation of the combined engine-exhaust aftertreatment system. Furthermore, upcoming on-board diagnostics regulations require on-board technologies to evaluate the status of the DPF. This work describes the application of radio frequency (RF) - based sensing techniques to accurately measure DPF particulate matter levels. A 1.9L GM turbo diesel engine and a DPF with an RF-sensor were studied. Direct comparisons between the RF measurement and conventional pressure-based methods were made. Further analysis of the particulate matter loading rates was obtained with a mass-based total PM emission measurement instrument (TEOM) and DPF gravimetric measurements.

A transient, one-dimensional lean NOx trap (LNT) model is described and implemented for vehicle systems simulations. The model accounts for conservation of chemical species and thermal energy, and includes the effects of O₂ storage and NOx storage (in the form of nitrites and nitrates). Nitrites and nitrates are formed by diffusion of NO and NO₂, respectively, into sorbent particles, and reaction rates are controlled by chemical kinetics and solid-phase diffusion. The model also accounts for thermal aging and sulfation by means of empirical correlations, which have been derived from laboratory experiments. Example simulation results using the Powertrain Systems Analysis Toolkit (PSAT) are presented.

Lean NOx Trap (LNT) catalysts can effectively reduce NOx from lean engine exhaust. Significant research for LNTs in diesel engine applications has been performed and has led to commercialization of the technology. For lean gasoline engine applications, advanced direct injection engines have led to a renewed interest in the potential for lean gasoline vehicles and, thereby, a renewed demand for lean NOx control. To understand the gasoline-based reductant chemistry during regeneration, a BMW lean gasoline vehicle has been studied on a chassis dynamometer. Exhaust samples were collected and analyzed for key reductant species such as H₂, CO, NH₃, and hydrocarbons during transient drive cycles. The relation of the reductant species to LNT performance will be discussed. Furthermore, the challenges of NOx storage in the lean gasoline application are reviewed.

Due to increasingly stringent emissions regulations, Lean NOx Trap (LNT) catalysts are being researched as a potential solution for diesel engine emissions reduction. LNTs are practical for diesel NOx reduction due to their ability to reduce NOx from the O2 rich environment produced by diesel engines. LNTs function by storing NOx on the catalyst surface during efficient lean operation then, under rich conditions, releasing and reducing the trapped NOx. One method of producing this rich environment which regenerates a LNT involves manipulating the fuel injection parameters and throttling the air intake. This process is called in-cylinder regeneration. Experiments will be described here in which a 1.7 L common rail diesel engine has been used to regenerate LNTs at various stages of sulfur exposure, a known poison of the LNT.

The influence of fuel rail pressure (FRP) and urea-selective catalytic reduction (SCR) on particulate matter (PM) formation is investigated in this paper along with notes regarding the NOx and other emissions. Increasing FRP was shown to reduce the overall soot and total PM mass for four operating conditions. These conditions included two high speed conditions (2400 rpm at 540 and 270 Nm of torque) and two moderated speed conditions (1400 rpm at 488 and 325 Nm). The concentrations of CO2 and NOx increased with fuel rail pressure and this is attributed to improved fuel-air mixing. Interestingly, the level of unburned hydrocarbons remained constant (or increased slightly) with increased FRP. PM concentration was measured using an AVL smoke meter and scanning mobility particle sizer (SMPS); and total PM was collected using standard gravimetric techniques. These results showed that the smoke number and particulate concentrations decrease with increasing FRP.

A Lean NOx Trap (LNT) regeneration method that has shown promise regarding its ability to effectively regenerate the LNT, while not adversely affecting the PM emissions, involves the use of Low Temperature Combustion (LTC). LTC is accomplished by highly diluting the intake charge with EGR.1-3* If enough EGR is applied, the in-cylinder air:fuel mixture, and ensuing exhaust, will become rich, thereby regenerating the LNT. This type of highly dilute combustion tends to be more premixed than diffusion, which can lower engine-out PM and NOx emissions. LTC regeneration has been characterized and results are presented comparing this approach to other approaches for rich, in-cylinder diesel combustion for LNT regeneration.

Hydrogen (H2) is an excellent reductant, and has been shown to be highly effective when introduced into a variety of catalysts such as three-way catalysts, lean NOx traps (LNTs), and hydrocarbon lean NOx catalysts (also termed hydrocarbon selective catalytic reduction (SCR) catalysts). Furthermore, since lean-burn engines offer improved fuel efficiency yet difficult NOx emission control, H2 production during lean operation for the purpose of NOx reduction could be beneficial. On-board generation of hydrogen is being explored via catalytic or plasma-based reformers. A possible alternative to these add-on systems is generation of the H2 in-cylinder with standard fuel injection hardware. This paper details experiments relating to the production and measurement of H2 under net-lean operation in a common-rail diesel engine. In-cylinder fuel control is used to tailor the combustion process such that H2 is generated while maintaining a lean Air:Fuel ratio in the bulk exhaust gas.

Advanced diesel combustion regimes such as High Efficiency Clean Combustion (HECC) offer the benefits of reduced engine out NOx and particulate matter (PM) emissions. Lower PM emissions during advanced combustion reduce the demand on diesel particulate filters (DPFs) and can, thereby, reduce the fuel penalty associated with DPF regeneration. In this study, a SiC DPF was loaded and regenerated on a 1.7-liter 4-cylinder diesel engine operated in conventional and advanced combustion modes at different speed and load conditions. A diesel oxidation catalyst (DOC) and a lean NOx trap (LNT) were also installed in the exhaust stream. Five steady-state speed and load conditions were weighted to estimate Federal Test Procedure (FTP) fuel efficiency. The DPF was loaded using lean-rich cycling with frequencies that resulted in similar levels of NOx emissions downstream of the LNT.

Alkali and alkaline earth metal impurities found in diesel fuels are potential poisons for diesel exhaust catalysts. Using an accelerated aging procedure, a set of production exhaust systems from a 2011 Ford F250 equipped with a 6.7L diesel engine have been aged to an equivalent of 150,000 miles of thermal aging and metal exposure. These exhaust systems included a diesel oxidation catalyst (DOC), selective catalytic reduction (SCR) catalyst, and diesel particulate filter (DPF). Four separate exhaust systems were aged, each with a different fuel: ULSD containing no measureable metals, B20 containing sodium, B20 containing potassium and B20 containing calcium. Metals levels were selected to simulate the maximum allowable levels in B100 according to the ASTM D6751 standard. Analysis of the aged catalysts included Federal Test Procedure emissions testing with the systems installed on a Ford F250 pickup, bench flow reactor testing of catalyst cores, and electron probe microanalysis (EPMA).

In this contribution, nuanced changes of a commercial Cu-SSZ-13 catalyst with hydrothermal aging, which have not been previously reported, as well as their corresponding impact on SCR functions, are described. In particular, a sample of Cu-SSZ-13 was progressively aged between 550 to 900°C and the changes of performance in NH3 storage, oxidation functionality and NOx conversion of the catalyst were measured after hydrothermal exposure at each temperature. The catalysts thus aged were further characterized by NH3-TPD, XRD and DRIFTS techniques for structural changes. Based on the corresponding performance and structural characteristics, three different regimes of hydrothermal aging were identified, and tentatively as assigned to “mild”, “severe” and “extreme” aging. Progressive hydrothermal aging up to 750°C decreased NOx conversion to a small degree, as well as NH3 storage and oxidation functions.

Previously reported work with a full-scale ethanol-SCR system featuring a Ag-Al2O3 catalyst demonstrated that this particular system has potential to reduce NOx emissions 80-90% for engine operating conditions that allow catalyst temperatures above 340°C. A concept explored was utilization of a fuel-borne reductant, in this case ethanol “stripped” from an ethanol-diesel micro-emulsion fuel. Increased tailpipe-out emissions of hydrocarbons, acetaldehyde and ammonia were measured, but very little N2O was detected. In the current increment of work, a number of light alcohols and other hydrocarbons were used in experiments to map their performance with the same Ag-Al2O3 catalyst. These exploratory tests are aimed at identification of compounds or organic functional groups that could be candidates for fuel-borne reductants in a compression ignition fuel, or could be produced by some workable method of fuel reforming.

The combination of advanced combustion with advanced selective catalytic reduction (SCR) catalyst formulations was studied in the work presented here to determine the impact of the unique hydrocarbon (HC) emissions from premixed charge compression ignition (PCCI) combustion on SCR performance. Catalyst core samples cut from full size commercial Fe- and Cu-zeolite SCR catalysts were exposed to a slipstream of raw engine exhaust from a 1.9-liter 4-cylinder diesel engine operating in conventional and PCCI combustion modes. The zeolites which form the basis of these catalysts are different with the Cu-based catalyst made on a chabazite zeolite which las smaller pore structures relative to the Fe-based catalyst. Subsequent to exposure, bench flow reactor characterization of performance and hydrocarbon release and oxidation enabled evaluation of overall impacts from the engine exhaust.

The combination of advanced combustion with advanced selective catalytic reduction (SCR) catalyst formulations was studied in the work presented here to determine the impact of the unique hydrocarbon (HC) emissions from premixed charge compression ignition (PCCI) combustion on SCR performance. Catalyst core samples cut from full size commercial Fe- and Cu-zeolite SCR catalysts were exposed to a slipstream of raw engine exhaust from a 1.9-liter 4-cylinder diesel engine operating in conventional and PCCI combustion modes. The zeolites which form the basis of these catalysts are different with the Cu-based catalyst made on a chabazite zeolite which has smaller pore structures relative to the Fe-based catalyst. Subsequent to exposure, bench flow reactor characterization of performance and hydrocarbon release and oxidation enabled evaluation of overall impacts from the engine exhaust.